Dunting is a fault that can occur during the firing of ceramic articles. It is the "cracking that occurs in fired ceramic bodies as a result of a thermally induced stress" and is caused by a "ware cooled too quickly after it has been fired". Although usually occurring during cooling dunts can also be caused by excessively fast heating rates. Heating dunts can be recognised by rounded edges to the cracks as the glaze matured after they occurred, whereas cooling dunts have sharp edges.
primaryTopic
Dunt
Dunting is a fault that can occur during the firing of ceramic articles. It is the "cracking that occurs in fired ceramic bodies as a result of a thermally induced stress" and is caused by a "ware cooled too quickly after it has been fired". Although usually occurring during cooling dunts can also be caused by excessively fast heating rates. Heating dunts can be recognised by rounded edges to the cracks as the glaze matured after they occurred, whereas cooling dunts have sharp edges.
has abstract
Dunting is a fault that can oc ...... rack during cooling.(Dunting)"
@en
Wikipage page ID
Wikipage revision ID
655,156,629
subject
comment
Dunting is a fault that can oc ...... ooling dunts have sharp edges.
@en
label
Dunt
@en